It is a stress crack.
I have been shooting Rem 7 Mags since 1977, never seen anything like this.
Two things would cause this:
Extremely hard brass
Oversize chamber firing work hardened brass
Brass defect-thin wall
If you have the devise from
www.sinclairintl.com that measures wall thickness, you could determine wall thickness at any point in the case.