I have a titanium Taurus .45 Colt with an aluminum anodized frame. I blasted the blue color off with 120gr aluminum oxide and coated it black. I have since read that the anodizing process adds strength to the aluminum finish should not be removed. Is this true? I have shot the gun some with no issues, and do know not to shoot hot loads in it. Ken
�Nothing is so permanent as a temporary government program." -- Milton Friedman
|
|
|
|
Joined: Nov 2012
Posts: 141
Campfire Member
|
Campfire Member
Joined: Nov 2012
Posts: 141 |
HArd anodizing will not increase the strength any appreciable amount. It will add corrosion and wear resistance but not any kind of strength.
Consider it unmodified and shoot as usual
|
|
|
|
Joined: Oct 2008
Posts: 7,821
Campfire Outfitter
|
OP
Campfire Outfitter
Joined: Oct 2008
Posts: 7,821 |
I like your answer. Thanks a lot, Ken
�Nothing is so permanent as a temporary government program." -- Milton Friedman
|
|
|
|
Joined: Jun 2001
Posts: 19,079
Campfire Ranger
|
Campfire Ranger
Joined: Jun 2001
Posts: 19,079 |
All anodizing does is make a layer of aluminum oxide a few thousandths deep on the aluminum.Basically ceramic. It adds durability to the finish,but not to the under lying material.
Last edited by saddlesore; 12/12/12.
If God wanted you to walk and carry things on your back, He would not have invented stirrups and pack saddles
|
|
|
|
Joined: Dec 2004
Posts: 10,345
Campfire Outfitter
|
Campfire Outfitter
Joined: Dec 2004
Posts: 10,345 |
|
|
|
|
Joined: Dec 2002
Posts: 15,860
Campfire Ranger
|
Campfire Ranger
Joined: Dec 2002
Posts: 15,860 |
All anodizing does is make a layer of aluminum oxide a few tenths of a thousandths deep on the aluminum. Basically ceramic. It adds durability to the finish,but not to the under lying material. As in .0002" roughly.
|
|
|
|
Joined: Feb 2010
Posts: 17,814
Campfire Ranger
|
Campfire Ranger
Joined: Feb 2010
Posts: 17,814 |
Anodizing as utilized on firearms is sulphuric anodizing that has been dyed black, it is approximately .0002" (two ten thousandths). It is a controlled oxidation similar to gun bluing (black oxide), its main function is to prevent further uncontrolled oxidation. It provides some protection from abraision though this is limited to its minimal depth, I would hesitate to call it ceramic though. Hard coat anodizing is another matter, it provides much more surface hardness and therefore resistance to attack from hostile environments. The drawback to hardcoat anodize is increased cost vs. sulphuric anodize, also it cannot be dyed the range of colors that sulphuric anodize can.
|
|
|
|
Joined: Nov 2012
Posts: 141
Campfire Member
|
Campfire Member
Joined: Nov 2012
Posts: 141 |
You mean Type 2 and 3. Type 2 can be as thin as .0001" to as thick as .001" under controlled highly specialized condition. Type 3 can be a few thousandths thick and is usually only available in clear or black. and it is a ceramic (� ( ceramic) any nonmetallic solid that remains hard when heated.) What you are doing is converting the aluminum to aluminum oxide the same stuff used in sand paper. And both type 2 and 3 can use sulfuric acid Type 3 is a different dilution of acid and the bath is refrigerated and the current density is much higher.
BAck on point though. Anodizing only add a layer of corrosion and wear resistance while also adding some cosmetic effects
|
|
|
|
602 members (10gaugemag, 12344mag, 1234, 10ring1, 007FJ, 10gaugeman, 54 invisible),
2,537
guests, and
1,253
robots. |
Key:
Admin,
Global Mod,
Mod
|
|
Forums81
Topics1,191,800
Posts18,477,464
Members73,944
|
Most Online11,491 Jul 7th, 2023
|
|
|
|
|