I'm pretty sure the method the OP described uses a candle. The "JB Method" uses a candle. If you think a candle is the same as a propane torch as far as the speed with which it heats the brass or the temperatures yielded, that's not my problem.
A wise man is frequently humbled.
|
|
|
|
Joined: Feb 2001
Posts: 5,958
Campfire Tracker
|
Campfire Tracker
Joined: Feb 2001
Posts: 5,958 |
As far as the original question goes, I usually do not see a color change from the candle method. Now, how much annealing is taking place? Who knows, but the cases are obviously softer when I trim/chamfer and I don't split necks, so it must be working.
I did have to laugh at all the answers you got about how to anneal NOT using the candle method. I'm sure that helped you immensely.
Don't just be a survivor, be a competitor.
|
|
|
|
Joined: Dec 2002
Posts: 12,321
Campfire Outfitter
|
Campfire Outfitter
Joined: Dec 2002
Posts: 12,321 |
To the OP:
I only started annealing a few years ago and my method is a propane torch and a small container of water.
My guess is that you are close to being perfect. Remember that a fast rate of cooling is nearly as important as the temperature. You want to freeze the alloy in an amorphous state.
I worked in a solder factory for a number of years and saw a lot of similar situations with copper alloys. It was hard keeping 3 shifts running the same amount of this or that, but the quality of the end-product remained high. I once did a study of the annealing of our wire and found a huge difference between the inner parts of a spool and the outer (we're talking 500 lb spools). However, the wire that came off the spool ended up being equally workable.
|
|
|
|
Joined: Jun 2006
Posts: 46,026
Campfire 'Bwana
|
Campfire 'Bwana
Joined: Jun 2006
Posts: 46,026 |
Remember that a fast rate of cooling is nearly as important as the temperature. You want to freeze the alloy in an amorphous state. As far as rifle cartridge brass goes, this runs counter to what I've read in a couple of different places, from people who know their stuff including JB and the instructional video below from Anneal-Rite: https://www.youtube.com/watch?v=EXLPGcSNyUs
A wise man is frequently humbled.
|
|
|
|
Joined: Jan 2005
Posts: 57,477
Campfire Kahuna
|
Campfire Kahuna
Joined: Jan 2005
Posts: 57,477 |
I'm not JB
But I suspect I've annealed well over 100K 223 cases over the years.
Propane torch, spin em in my fingers in a dark room until I see the red color coming on which is also getting fairly hot to my fingers, drop in bucket/bowel of water on the kitchen table.
Never had a problem. And I had to have good accuracy and case life for my uses.
We can keep Larry Root and all his idiotic blabber and user names on here, but we can't get Ralph back..... Whiskey Tango Foxtrot, over....
|
|
|
|
Joined: Jan 2008
Posts: 422
Campfire Member
|
Campfire Member
Joined: Jan 2008
Posts: 422 |
dropping the cases in water will not hurt but it is not necessary to stop the heat suddenly for cartridge brass...
When a column of troops under Lt. Col. Francis Smith moved into the countryside to collect arms and munitions gathered by the patriot militia, hostilities erupted at Lexington and Concord on Apr. 19, 1775.
|
|
|
|
Joined: Apr 2014
Posts: 36
Campfire Greenhorn
|
Campfire Greenhorn
Joined: Apr 2014
Posts: 36 |
I previously spun them in my fingers, but for the last several years do it differently. I made a simple shell holder with a deep socket and spin it in a cordless drill. I anneal it with a propane torch in a dark room until the neck just begins to change color. It then get dumped in a dry bucket, no quenching here. Propane torch here as well. Works well for me.
Last edited by RollnBones; 04/19/14.
Brad Dana
|
|
|
|
Joined: Jul 2001
Posts: 60,098
Campfire Kahuna
|
Campfire Kahuna
Joined: Jul 2001
Posts: 60,098 |
Just got back from a hunting trip and have several comments:
1) NO, THE CANDLE METHOD IS NOT MY METHOD. I have repeatedly written that it was developed by Fred Barker, who wrote an article for Precision Shooting about using Tempilaq and hand-holding the case over a candle to develop an uncomplicated method of annealing that works.
Fred did NOT say it was the fastest method, but he did enough testing to make sure it worked. He also did NOT adjust the hold according to the length of the brass, because all finger-holding it does is assure the case head doesn't over-heat. Holding any case halfway down works, because the method "adjusts" for the length ad thickness of the case.
2) If you want to anneal faster a torch works better, but the color of the brass (either during or after heating) is a poor indicator of success. Both tend toward over-annealing. Any sort of temp-indicator paint works better.
In fact cartridge brass can anneal at 500 degrees if heated long enough. The 700-750 degree temp usually used is where it anneals fastest--but if you heat it too fast it will also tend to over-anneal and become too soft, because the zinc in the alloy starts to melt out. That's why the neck/shoulder area of over-annealed brass tends to change color.
Some factory brass is somewhat over-annealed, because a softer neck allows the brass to be loaded more times before it requires annealing. But that doesn't mean softer brass will be more accurate than brass annealed not as soft, more frequently.
3) The only reason for water-quenching is to keep the head from over-heating and hence annealing. If you stand the HEADS of cases in water it won't, and it also won't if you hold it halfway up the body and drop it. But there's no reason to quench the neck after heating.
“Montana seems to me to be what a small boy would think Texas is like from hearing Texans.” John Steinbeck
|
|
|
|
Joined: Dec 2002
Posts: 12,321
Campfire Outfitter
|
Campfire Outfitter
Joined: Dec 2002
Posts: 12,321 |
Wow. I stand corrected.
Learn something new every day.
|
|
|
|
Joined: Nov 2013
Posts: 3,779
Campfire Tracker
|
OP
Campfire Tracker
Joined: Nov 2013
Posts: 3,779 |
John
Thanks for the response and the good info. I hope you had a great trip. This thread got pretty out of hand, I'm glad you set the record straight. Sorry if I started people thinking this was your personal method, I posted that you described the method in your book, guess I shouldn't have been so obtuse.
Thanks again
Brandon
|
|
|
|
Joined: Jul 2001
Posts: 60,098
Campfire Kahuna
|
Campfire Kahuna
Joined: Jul 2001
Posts: 60,098 |
Brandon,
No problem. I always mention that Fred Barker developed the method and published an article about it, but people still tend to call it my method, probably because more people have read my writing on it than Fred's lone article in a small-circulation magazine.
Brass is interesting stuff, one of the few metal alloys that doesn't require quenching after annealing.
“Montana seems to me to be what a small boy would think Texas is like from hearing Texans.” John Steinbeck
|
|
|
|
111 members (01Foreman400, 338Rules, 406_SBC, 1minute, 1_deuce, 15 invisible),
1,542
guests, and
912
robots. |
Key:
Admin,
Global Mod,
Mod
|
|
Forums81
Topics1,191,493
Posts18,472,090
Members73,936
|
Most Online11,491 Jul 7th, 2023
|
|
|
|