that you find today. When I cast thousands of bullets for handguns about 40 years ago I used mostly wheel weights with good success. Now I find that wheel weights are vastly different. When I melt them down there is a huge amount of 'sludge' forming on the surface of the molten metal. Is this zinc? What to you guys do with it? It's a real pain and I have 7 five gallon buckets of wheel weights that I will eventually melt down if I live long enough.
It's going to be a real pain to have to sort through them but if that's what it takes to remove the weights that are not lead then I have no choice, I suppose.
I'm beginning to cast bullets for my 30-30 and .300 Savage and I am using a Lee Production pot with a setting of about 6-7. I find the driving bands on the bullets are not fully filled out and I suspect I need the lead to be hotter. Right?
I've read of so many that use Lee equipment but I just can't get the idea out of my head that lower priced equipment will not perform as well as Lyman, Redding-Saeco and RCBS. I am not trying to 'cheap out' and have no aversion to spending if it will give me better results.
Any advice you can give will be most appreciated. Many thanks, Mickey
|
|
|
|
Joined: Apr 2010
Posts: 2,385 Likes: 1
Campfire Regular
|
Campfire Regular
Joined: Apr 2010
Posts: 2,385 Likes: 1 |
Mickey, I've seen your recent questions and thought you were a newbe like me and maybe we could learn casting together but now find out you are an "old hat" at it. I think I read somewhere that the melting point of lead and zinc are about 50 degrees different and that zinc is higher....so keeping temp just high enough to melt the lead you can skim the zinc off the top? I'm sure someone who knows much more than me will be along soon to answer for both of us. I hope to cast my first 30-30 bullets soon.
Good Luck to you, Rick
Last edited by RickinTN; 11/16/12.
|
|
|
|
Joined: Jul 2004
Posts: 13,250
Campfire Outfitter
|
OP
Campfire Outfitter
Joined: Jul 2004
Posts: 13,250 |
Rick, While I cast lots of bullets a long time ago I am, by no means, up to speed on things. I am going to try a higher temp and see how that works.
I've about grown tired of the constant flow of 'fertilizer' at the Hunter's Campfire and think I'll hang out here for a time. In the meantime if you can imagine any way I might be of help to you don't hesitate to let me know.
Many thanks, Mickey
|
|
|
|
Joined: Dec 2008
Posts: 3,079
Campfire Tracker
|
Campfire Tracker
Joined: Dec 2008
Posts: 3,079 |
My understanding is that the zinc is corrosive in some manner and is undesirable in the the alloy. I have always heard that it makes for ugly bullets due to not filling the mold properly. I don't really know because I don't allow it to melt in the mix. I get just enough heat to melt the lead and everything else floats. When I do large quantities I just scoop everything off that doesn't melt right away.
Alan
Food is at the core of Hunting and Fishing - Rebecca Gray
|
|
|
|
Joined: Dec 2005
Posts: 457 Likes: 2
Campfire Member
|
Campfire Member
Joined: Dec 2005
Posts: 457 Likes: 2 |
The bullets are not filling out because of the zinc. Take what ever lead you have melted to the scrap yard and get rid of it.
Now you are going to have to sort all of the WW. I use a large pair of side cutters. The zinc will not cut. Find a radio station you like and sit down and try to cut each one. You don't have to cut them in half. Just see if the cutter will cut into them. The zinc will feel like trying to cut a 1/2" bolt. It will hardly even scratch it. There is also iron WW. The zinc ones will be marked Zn, the Iron ones will be marked Fe. But not always. There is no way around this. This is all from the tree huggers.
|
|
|
|
Joined: Jul 2004
Posts: 13,250
Campfire Outfitter
|
OP
Campfire Outfitter
Joined: Jul 2004
Posts: 13,250 |
I guess I'll have to bite the bullet (as soon as I cast one ![wink wink](/ubbthreads/images/graemlins/default/wink.gif) ) and sort through them. Thanks, guys.
|
|
|
|
Joined: Jul 2004
Posts: 13,250
Campfire Outfitter
|
OP
Campfire Outfitter
Joined: Jul 2004
Posts: 13,250 |
Alan, Can I not melt the lead/zinc mix and skim the zinc off if I keep the temperature below the melting point of zinc and eventually purify the lead? I won't hesitate to throw it out if there's no other way. Thanks.
|
|
|
|
Joined: Aug 2002
Posts: 19,136 Likes: 6
Campfire Ranger
|
Campfire Ranger
Joined: Aug 2002
Posts: 19,136 Likes: 6 |
My very limited experience with casting wheel weights led me to watch the pot carefully when I put the weights in, and you could tell the slow melters and remove them. Once I had some melted lead in the pot I would add one weight at a time, lead would melt quick and the zinc not, and I would remove it. miles
Look out for number 1, don't step in number 2.
|
|
|
|
Joined: Aug 2002
Posts: 19,136 Likes: 6
Campfire Ranger
|
Campfire Ranger
Joined: Aug 2002
Posts: 19,136 Likes: 6 |
I also noticed a rubbery like substance in the skim and thought that maybe some had a thin rubber coating, but it could have been road grime. miles
Look out for number 1, don't step in number 2.
|
|
|
|
Joined: Dec 2000
Posts: 10,353
Campfire Outfitter
|
Campfire Outfitter
Joined: Dec 2000
Posts: 10,353 |
zinc is not corrosive, it just causes wrinkles in the cast bullets and voids. These voids are detrimental to any type of accurate shooting.
If you keep your melt below the melting point of zinc it will float on the top and can be skimmed off easy enough. Once it's melted in, well, time to get new lead. Just keep the melt below 700� F and the zinc won't melt in.
I've done this numerous times, a thermometer helps and heat slowly, you'll be fine.
Whatever you are willing to put up with, is exactly what you will have.
When your ship comes in. ... make sure you are willing to unload it.
PAYPAL, sucks and I will never use them again. I recommend you do the same.
|
|
|
|
Joined: Dec 2000
Posts: 10,353
Campfire Outfitter
|
Campfire Outfitter
Joined: Dec 2000
Posts: 10,353 |
Lee production bottom pour 20lb pots are a great deal! It works well even though it's cheap don't be thrown off. I have one and it's great! Yes if the drive bands are not filled out, use more heat on the mould. if you head over to castboolits you'll be able to find the answers to all of your questions and more. Newbies are welcome over there. http://castboolits.gunloads.com/
Whatever you are willing to put up with, is exactly what you will have.
When your ship comes in. ... make sure you are willing to unload it.
PAYPAL, sucks and I will never use them again. I recommend you do the same.
|
|
|
|
Joined: Dec 2000
Posts: 10,353
Campfire Outfitter
|
Campfire Outfitter
Joined: Dec 2000
Posts: 10,353 |
the WW's these days have a "coating" on them, it's a plastic of sorts, it forms sludge on the top, just skim it off.
sawdust is a good flux along with old candles, add, light, stir, skim.
once something is melted into the lead, there's no getting it out.
Whatever you are willing to put up with, is exactly what you will have.
When your ship comes in. ... make sure you are willing to unload it.
PAYPAL, sucks and I will never use them again. I recommend you do the same.
|
|
|
|
Joined: Jul 2004
Posts: 13,250
Campfire Outfitter
|
OP
Campfire Outfitter
Joined: Jul 2004
Posts: 13,250 |
I upped the temperature this morning and the bullets were much better. My pot leaks as all Lee bottom pour pots do and I've twisted the rod that seats in the orifice and it still leaks. Not a big deal but still aggravating.
I've begun sorting my weights and have gotten almost to the point that I can spot a zinc weight but still use a pair of lineman's pliers to test them. That was a great suggestion that I didn't know about. Thanks for that tip.
|
|
|
|
Joined: Aug 2003
Posts: 37
Campfire Greenhorn
|
Campfire Greenhorn
Joined: Aug 2003
Posts: 37 |
Hi.Micky Have been melting wheel weights for 40 yrs. I run my pot at about 650deg. and skim of the top. I make 45, 38 and 357 pistol bullets and 45-70 rifle. I have no problem with wheel weights.
Last edited by DGarfield; 11/17/12. Reason: goffed
Dwayne Garfield
|
|
|
|
Joined: Dec 2008
Posts: 3,079
Campfire Tracker
|
Campfire Tracker
Joined: Dec 2008
Posts: 3,079 |
Mickey, I don't think there is any practical way to get the zinc out, or the lead for that matter. Pour what you got mixed and use it for plinking and then just be careful not to get any more in there. There's an awful lot about casting that I don't know. Certainly fluxing and skimming are recommended to a point but you can also skim the tin and antimony out too, and you may not want that.
The way I cast is very unscientific, but I do try not to melt any zinc in the pot. I use my production pot to melt everything down and test all WW with cutters as has been mentioned. I found the bulk melting in an old frying pan to be counterproductive in the amounts I deal with.
Alan
Food is at the core of Hunting and Fishing - Rebecca Gray
|
|
|
|
Joined: Jul 2004
Posts: 13,250
Campfire Outfitter
|
OP
Campfire Outfitter
Joined: Jul 2004
Posts: 13,250 |
Alan, the question keeps coming up in my mind how can you get the tin and antimony out and not get the zinc out? I had a "sludge" form on the top of my pot that I skimmed off and I assumed that was zinc. It was quite a bit but once I had that removed I could flux as always. I'm sorting through the WW now and picking out the zinc. Thanks for your help.
|
|
|
|
Joined: Jul 2004
Posts: 13,250
Campfire Outfitter
|
OP
Campfire Outfitter
Joined: Jul 2004
Posts: 13,250 |
Hi.Micky Have been melting wheel weights for 40 yrs. I run my pot at about 650deg. and skim of the top. I make 45, 38 and 357 pistol bullets and 45-70 rifle. I have no problem with wheel weights. Isn't Reed G. your uncle? How are y'all doing up there?
|
|
|
|
Joined: Aug 2003
Posts: 37
Campfire Greenhorn
|
Campfire Greenhorn
Joined: Aug 2003
Posts: 37 |
Hi Micky.
Reed is my younger brother. I don,t know how fast you plan on shootin your cast bullet, but I skim of what ever comes to the top and throw it. You can flux it first and then skim it, I use parfin wax to do mine, if you light it when it melts it won,t smoke. Have fun.
Dwayne
Dwayne Garfield
|
|
|
|
Joined: Jul 2004
Posts: 13,250
Campfire Outfitter
|
OP
Campfire Outfitter
Joined: Jul 2004
Posts: 13,250 |
I'm having a problem deciding if I want to use tumble lube or a sizer. When I cast many years ago I had a Lyman sizer and there's just something in the back of my mind that makes me want to stay in that mode. I do like Lee sizing dies but there's no way to fill the grooves with lube unless I use a kake kutter and that's too tedious.
I did some work for Reed a few years back. Please give him my regards the next time you speak with him. Thanks, Mickey
|
|
|
|
Joined: Aug 2003
Posts: 37
Campfire Greenhorn
|
Campfire Greenhorn
Joined: Aug 2003
Posts: 37 |
To Micky
try this sight it is very good. The Los Angles Silhoutte Club
Dwayne Garfield
|
|
|
|
74 members (325wsm1, 10gaugemag, 35, 6mmbrfan, 12 invisible),
13,765
guests, and
1,107
robots. |
Key:
Admin,
Global Mod,
Mod
|
|
Forums81
Topics1,195,229
Posts18,544,002
Members74,060
|
Most Online21,066 May 26th, 2024
|
|
|
|